lath martensite 中文意思是什麼
lath martensite
解釋
板條馬氏體- lath : n （pl laths ） 【建築】板條，板樁。 a lath and plaster shed （木架）板條，灰面屋。 a lath painte...
- martensite : n. 馬丁體〈顯微鏡下所見的煉鋼的針狀組織〉。adj. -sitic
-
The lath martensite nanometer structure can play the role of fine - particle strengthening and dislocation strengthening as well as coordinate the distribution of dislocation. it is hopeful that the strength and toughness of material with this structure can be increased at the same time
板條馬氏體組織納米化結構，可起到納米晶粒的細晶強化與位錯強化的聯合作用，並可協調位錯分佈，有望使具有這種組織的材料強度和韌性同時得以提高。 -
The result shows that tempered martensite has apparent lath character when temper is between 740 ~ 780, and the hardness of welded joint is 264 ~ 237hv, which can get better performance of the welded joint the lath character of martensite in welded joint disappears, and the carbide in the tempered sorbite of the base metal will aggregate when temper temperature is above 780, and the hardness and plastic property will reduce obviously
結果表明，在740 ~ 780之間回火，焊縫硬度為264 ~ 237hv ，回火馬氏體板條特徵明顯，可以獲得優良的焊接接頭性能；回火溫度超過780 ，焊縫板條馬氏體特徵消失，母材回火索氏體中碳化物產生偏聚，硬度、塑性明顯降低。 -
The result showed that plastic deformation during pre - strain played an restrained role on the growth of martensite ( especially in the direction of lath width ) and increase the nucleation rate indirectly ; the elastic energy induced by plastic deformation restrain the transformation of primary martensite but accelerate the transformation of after martensite
實驗結果表明：預應變過程中造成的塑性變形對馬氏體生長（尤其是寬度方向）有約束作用，起間接提高馬氏體形核率的作用，所儲備的彈性應變能對初生馬氏體的轉變有抑制作用，但對繼生馬氏體的轉變卻有促進作用。 -
The lath width of martensite can be fined noticeably by pre - strained quenching at non - dynamic recrystallization to approach nanometer magnitude ( the average width is 120nm )
採用非動態再結晶溫度下的預應變-淬火，提高馬氏體相變形核率，可以超細化馬氏體的板條晶片寬度，使之接近納米量級水平（平均寬度達到120nm ） 。