On the base of the analysis on the advanced technology of hard ferrite in foreign country, the main procedures of preparing hard ferrite pre - sintering material are determined as follows : first, the ferrite oxides coming from the main cold rolling line and strontium carbonate are conveyed to storage tank by gas power and weighed automatically according to the demands of constituent composition. and then they are mixed and grinded by using method of wet treatment. finally the mixtures is transported to the devices of storage by transporting pump
在分析國外先進的永磁鐵氧體生產工藝的基礎上，確定了生產高檔永磁鐵氧體預燒料的主要過程：首先，利用攀鋼冷軋鐵紅為主要原料，將氧化鐵紅及碳酸鍶採用氣力輸送至貯料料倉，經自動稱量裝置，按工藝配方稱量後分別由氧化鐵紅及碳酸鍶發送罐氣力輸送進入預混攪拌筒加水攪拌，然後再送入混磨機濕法混磨；最後，混合物經輸送泵輸送至料漿存儲裝置，經定量進料泵定量輸送至回轉窯進行濕法預燒，預燒料經緩冷至室溫后，再球磨。 -
Baseing on the request of low coercivity and high squareness in application, we had confirmed the main formulation of the lizn ferrite ; during the study of the conventional ceramic process, with the main formula foundation, we mainly studied the influence of ti4 +, co3 + on lowering coercivity and bi2o3, v2o5 on lowering sinter temperature. the results showed bi2o3 good characteristic on lowering sinter temperature and the sample which mixed with 1 % bi2o3 could reduce 40 % coercivity through slowing heating rate and extending the holding time
在氧化物陶瓷工藝技術研究中，按實際應用中低矯頑力、高矩形比的要求，確定了lizn鐵氧體的主配方，在主配方基礎上進行了ti4 + 、 co3 +等離子對降低矯頑力的研究以及添加bi2o3 、 v2o5助熔劑對降低燒結溫度的研究，發現bi2o3具有優良的降低燒結溫度的特性，在添加bi2o3樣品燒結過程中，降低升溫速率，延長保溫時間可以降低40 %左右的矯頑力。 -
The experiments showed us : firstly, mediums with different magnetic and dielectric properties had different influence on the microwave - absorbing properties of spinel ferrite ; secondly, magnetic texture treatment greatly affected the microwave - absorbing properties of the spinel ferrite - based mixed material which contained single - domain particles of hexagonal ferrite, changing the matching thickness, the density of area and the position of absorption peaks and increasing the absorption quantity and the 10db bandwidth ; thirdly, the coupling effect between different layers affected the microwave - absorbing properties of the double - layer spinel ferrite - based mixed material, decreasing its matching thickness and density of area and increasing the position of absorption peaks
實驗發現： （ 1 ）不同磁性與電性的介質對尖晶石型鐵氧體吸波特性的影響不同； （ 2 ）磁織構化處理對含有六角晶系鐵氧體單疇顆粒的尖晶石型鐵氧體基混合吸波材料的性能影響很大，可以改變匹配厚度、面密度與吸收峰峰位，提高吸收量與10db帶寬； （ 3 ）對于雙層材料，層間耦合作用會影響其吸波性能，降低匹配厚度與面密度，提高吸收峰峰位。 -
In addition, we also studied the influence of magnetic texture treatment, double - layer structure and medium film on the spinel ferrite - based mixed material
同時，初步研究了磁織構化處理、雙層結構及介質膜對尖晶石型鐵氧體基混合吸波材料性能的影響。 -
In this dissertation, high permeability mn - zn ferrites have been prepared by the mixed - oxide route, using mn3o4, fe2o3 and zno as the raw materials. and in this dissertation we study deeply on the preparation technology and mechanism of high initial permeability mnzn ferrite with better stability of which the initial permeability was 10000
本文採用氧化物陶瓷工藝制備高磁導率mnzn鐵氧體，以mn3o4 、 fe2o3和zno為原料，對磁導率為10000且具有寬頻特性的高磁導率mnzn鐵氧體的制備技術和機理進行研究。 -
The single layer films are physically mixed and prepared by polychloroprene and ferrite 94rc. one is synthesized in a lump, the maximal value of its inverse absorption is 12. 88db but the obverse is 8. 54db at 6. 79ghz ; the absorption band of its inverse is wider than another side. the other films are made by quartic equal steps, the absorption of its obverse and inverse have not too much differences, the peak value is 10db at 14. 4ghz
吸波性能測試表明一次注模所制薄膜其反面在8 . 88ghz時有最大衰減12 . 88db ，而正面在6 . 79ghz時有最大衰減8 . 54db ，反面的吸波頻帶也比正面寬;而四次注模所制薄膜其吸波性能在正反兩面的吸收頻帶和強度基本一致，在14 . 4ghz時達到10db左右。