Indium stannum oxide ( ito ) as semiconductor have caused a great deal of interest due to their prominent electro - optical behavior. ito has high prominent transmittance, high infrared reflectance, good electrical conductivity, ito applied as gas sensors, photovoltaic devices, heat reflecting mirrors, solar cells, flat panel displays, liquid crystal displays, electroluminescent, devices and organic light - emitting diodes ( oled ) etc. although preparations and applications of ito films have been studied deeply. nano - ito composites hardly studied
氧化銦錫（ ito ）是一種高簡並的n型半導體，由於具有導電性，可見光高透過率，紅外反射性，穩定的化學性，被廣泛應用於熱反射建築玻璃、抗靜電塗層，太陽能電池，熱發射鏡，平板顯示器和液晶顯示屏，傳感器，有機光致二級管（ oled ）等方面，國內外對高質量的ito薄膜的制備和應用進行了深入的研究，但是很少有ito納米粒子與高分子材料復合的報道。 -
The design of amorphous photonic material and photonic crystal devicements we design to make a reflecting mirror of cylinder paraboloid of an antenna by using amorphous photonic materials. we calculated the transmission of the mirror and the distribution of electric field by using multiple scattering method. the result shows that it can be used as a reflecting mirror of an antenna
非晶光子材料和光子晶體器件的設計提出了用介質圓柱光子晶體作微波天線的柱拋物面反射鏡，用多重散射方法計算了反射鏡的透過譜，並模擬計算了天線的電場分佈，初步認為可以用非晶光子材料作微波天線的反射鏡。 -
The infrared results showed that the ir characteristic value l080cm - lof cubic crystal sio, and the absorption peak 460cm - l of mgf, caused by the interaction between f - - mg ' + - p elastic vibration and photon radiation, appeared in the ir spectra. ellipsometric analysis showed that the typical absorption peaks 58lnm, 589nm and 606nm, resulting from the surface plasma resonance of cu panicles and reflecting the absorption on composite film system, appeared in the extinction coefficient k curves of cu ( voll5 % ) mgf, cu ( vol20 % ) mgf, and cu ( vol30 % ) mgf, cermet films, respectively. with the component of cu increasing, the peak site presented red shift, which was in accordance to the results of ultraviolet - visible spectra
橢偏測試分析表明： cu （ vol15 ） mgf _ 2 、 cu （ vol20 ） mgf _ 2和cu （ vol30 ） mgf _ 2樣品的消光系數k曲線中出現了反映復合金屬陶瓷體系吸收的由cu金屬顆粒表面等離子體共振引起的吸收峰，峰位分別為581nm 、 589nm和606nm ，呈現紅移，這些與紫外-可見光譜測試結果相一致；此外， cu - mgf _ 2復合納米金屬陶瓷薄膜光學常數的實驗值與考慮尺寸效應修正過的mg理論值總體上符合得很好。