  1. Blowout reason analysis of low - temperature superheater tube

    低溫段過熱器管爆裂原因分析
  2. Results show that the tube - burst is mainly due to the result of tube ' s long term overheating, while the main causes resultsing in overtemperature of the platen superheater are as follows ; ( 1 ) burn - out of superheater ' s pipe - grippers ; ( 2 ) some tube - sections are out of the row ; ( 3 ) unsuitable mode for adjusting the desuperheating water

    結果表明：爆管主要是由於管子長期過熱所致，而屏式過熱器管卡燒損、個別管段出列、減溫水調節方式不當是引起屏式過熱器超溫的主要原因。
  3. Failure diagnosis after changing tube for last stage superheater of boiler

    鍋爐末級過熱器換管后失效診斷
  4. This temperature calculation method avoids the non - correspondence between the flow rate and heat flux, which may exists in that used by boiler manufactures, and was employed to calculate the tube temperature of dangerous position that concerns with the retrofit scheme of superheater 1 of tower type coal - fired 330 mw once - through boiler in pucheng power plant for 100 % and 50 % operation load

    針對蒲城電廠330mw塔式燃煤直流鍋爐1號過熱器的改造方案，利用本文提出的方法與電廠鍋爐常用的壁溫計算方法分別計算了100 %與50 %鍋爐運行負荷下危險部位的壁溫。
  5. In the end of the dissertation, a tube lifetime evaluation software system is developed with the utility of the finite element analysis stress computation and the metallographic tests. the lifetime of the platen superheater tube is evaluated by the software system

    最後，綜合以上應力解析法、有限元應力計算和余相試驗研究開發了管件壽命評估軟體系統，並使用該系統綜合評估了屏式過熱器管段的壽命。
  6. Directing against tube - burst problem of austenitic stainless steel pipe in final stage superheater of boiler no. 1 in one power plant, it is believed that the main cause to be peel - off of oxide skin from inernal wall of steel pipe and blockage in the said tube through macroscopic examination, metallurgical analysis and oxide skin inspection

    摘要針對某電廠1號鍋爐末級過熱器奧氏體不銹鋼管爆管問題，通過宏觀檢驗、金相檢驗和氧化皮檢測，確定其主要由鋼管內壁氧化皮脫落堵塞所致。
  7. Through experimental detection methods of macro inspection, chemical composition analyzing, mechanic performance testing, micro metallography analyzing and x ray diffraction, the blowout reasons of low - temperature superheater tube were analyzed in the process of boiler operation

    摘要通過宏觀檢查，化學成分分析，機械性能測試，金相檢驗和x射線衍射等試驗檢測方法，對鍋爐運行過程中低溫段過熱器管爆裂原因進行了分析。
  8. This model correctly judges the slagging tendency of a kind of coal - water slurry. measurements are taken of the temperature field, flame emissivity, superheater tube wall temperature, exhaust gas temperature and composition

    本文介紹了燃油鍋爐改燒水煤漿后爐內傳熱及其污染物的排放測試結果，包括溫度場、火焰黑度、過熱器管壁溫度、排煙溫度、排煙成分。
  9. Superheater, reheater and economizer are the main component of the heat exchangers in boiler. whether they run safely and stably or not is directly count for much the safe of the whole plant operation. and the frequent tube leakage of heat surface impact upon the economy benefits and the society benefits of the power plant

    水冷壁管、過熱器管、再熱器管、省煤器管（ 「四管」 ）是鍋爐內部的主要受熱面結構件，它們是否安全穩定的運行直接關繫到整個電廠的安危，頻繁爆漏事故影響了電廠的經濟效益和社會效益。
  10. It is researched that the influence on the tube lifetime of the metallographic structure and the alloy element and the rigidity by the test the superheater and reheater tube which is made of 12cr2mowvtib steel. the metallographic change after the tube has run in the high temperature and high pressure condition for long time is more believable and frank than the intensity lifetime analysis to evaluate the tubes remain lift time

    然後，通過試驗研究了過熱器和再熱器管12cr2mowvtib鋼材的金相組織、合金元素和硬度等對管道壽命的影響，分析管材在高溫高壓下長期運行后金相組織的變化情況，對管材定性壽命評估，這種與強度壽命分析完全不同的方法直觀可信的展示了材料損傷狀況。
  11. It is researched that the influence on the tube lifetime of the metallographic structure and the alloy element by testing the superheater and reheater tube which is made of 12cr2mowvtib steel. the metallographic change and the distribution of alloy elements after the tube has run in the high temperature condition for longtime is more believable and franker to evaluate the tubes remain life time

    然後，通過試驗研究了過熱器和再熱器管12cr2mowvtib鋼材的金相組織、合金元素對管道壽命的影響，分析了管材在高溫長期運行后金相組織和合金元素分佈的變化情況，對管材壽命進行定性評估。
  12. Through macroscopic examination, wall - thickness measurement, and metallographic examination of tube specimen taken from the bursted platen superheater of boiler no. 1, the causes leading to tube - burst have been analysed

    摘要通過對1號爐屏式過熱器爆管管樣的宏觀檢驗、壁厚測量和金相檢驗，對爆管原因進行了分析。
  13. On the basis of the reptured tube at the final superheater of no. 4 boiler in yangluo power plant, the " tee junction effect " of terminal header on flux distribution in superheater was analysed, a mathematical model was founded to calculate the tube temperature and evaluate the lifespan of superheater and some measures to prevent eddy current in the area near the tee junction were put forward

    摘要分析了進口等徑三通對過熱器管流量分配的影響，建立了過熱器壁溫計算模型，並以華能陽邏電廠4號爐高溫過熱器爆管為例，對渦流效應的大小進行了分析，提出了消除渦流效應的措施。