  1. Following is the factors ideating with the surface of old concrete in different way ( including brushing surface, chiseling surface, cleaving surface ), adherence agent ( including cement slurry, cement sand slurry, cement slurry with the u expansion agent ), the freeze - thaw circulation times and air - entraining. as a result, we found that the roughness influence on the adhesion capability of the new on old concrete to a large degree. the larger rougeness is, the larger the splitting tensile strength on the adhension face is. the kind of adhesion agent is also influence on the adherence capability of new on old concrete. the circulation times of freez - thaw have a large influence on the splitting tensile strength of adherence face of new on old concrete. the analysis of tests give some advices to the practical engineering

    主要考察了老混凝土表面不同處理方式（刷毛面，鑿毛面，劈裂面） 、界面粘結劑類型（水泥凈漿，水泥砂漿， u型膨脹劑水泥漿） 、凍融循環次數等對新老混凝土粘結面劈拉強度的影響，以及凍融作用下新混凝土加氣對粘結面劈拉強度的影響。試驗結果表明，粗糙度對新老混凝土粘結性能有重要影響，隨著粘結面粗糙度的增大，粘結面劈拉強度不斷增加；界面粘結劑類型對新老混凝土粘結性能有一定影響，在凍融作用下， u型膨脹劑水泥漿粘結效果不如水泥凈漿和水泥砂漿；凍融循環對粘結面劈拉強度有較大影響，加氣能明顯改善新老混凝土粘結面的抗凍能力。
  2. Based on the close packing and grain composition theory, a new anti - gas channeling lightweight high performance cement slurry system has been developed with industrial drift beads as lightweight additive and superfine gel as strengthening agent

    摘要基於緊密堆積和顆粒級配理論，研製了一種以工業漂珠為減輕劑、以超細膠凝材料為增強劑的新型低密度、高強度防氣竄水泥漿體系。
  3. ( 2 ) interfacial agents this experiment adopts three types of interfacial agents : no interfacial agent, neat cement paste which has the same water - cement ratio with the new concrete, cement paste mixed with 10 % expanding agent which has the same ratio with the new concrete ( which is called cement paste mixed with expanding agent for short ). the thickness of the interfacial agent is 2 ~ 3mm

    （ 2 ）粘結劑本試驗採用三種粘結劑：無粘結劑、同新混凝土相同水灰比的水泥凈漿、摻10 u型膨脹劑的同新混凝土相同水灰比的水泥凈漿（以下簡稱水泥膨漿） 。界面劑的厚度一般為2 3mm 。
  4. The results of research work show that the values of sand rate, aggregate grading, paste content and mineral admixtures control the degree of tightness pile up and the workability of fresh concrete, furthermore, they determined the mechanics performance and the durability of self - compacting concrete

    研究表明，砂率、集料級配、水泥漿量、礦物摻合料等因素的取值決定了免振搗混凝土的緊密堆積程度及新拌混凝土的工作性能，從而進一步決定了免振搗混凝土的物理力學性能及耐久性能。
  5. Analytical solution of the nearest surface spacing between neighboring binder grains in fresh cement paste

    新拌水泥漿體中鄰近膠凝材料粒子表面最近間距分佈的解析解
  6. With the retrospection of the developing course of the bored pile foundation and combining with my practical experience, the paper expatiates upon the design principle of percent of fit of the stone - fill grouted concrete and the main factors of the influence strength target, and the final pile technique introduction of the hollow pile of the stone - fill grouted concrete and the precast prestressed concrete ; baesd on the theory of slurry hydraulics, empirical calculation formulas of the radis and height of diffuse slurry are deduced in this paper ; it analyzes the test pile materials of the hollow pile foundation, such as luoyang yi river bridge and dangwang jian river bridge ; the new technique of the hollow pile, which provides the generalization and application with base materials, expounds its feasibilities, adaptabilities and economy

    本文通過綜合分析國內外鉆孔樁基礎的發展歷程及研究現狀，重點討論了填石壓漿混凝土空心樁、預制預應力混凝土空心樁的成樁工藝、填石壓漿混凝土的配合比設計原理及影響強度指標的主要因素；根據泥漿水力學原理，導得了考慮各種因素的水泥漿液在預填骨料中的流動影響半徑和上升高度；結合河南省洛陽伊河大橋、黨灣澗河大橋工程實踐，討論了填石壓漿混凝土空心樁基礎的質量檢測方法及標準；並在此基礎上，深入分析了樁側、樁端承載能力，提出了填石壓漿混凝土空心樁的設計計算理論和方法。最後，論證了空心樁新工藝的可行性、適應性、經濟性，為大力推廣應用空心樁新技術提供了可靠的技術資料。
  7. In the paper the effects of the made parameters, the main materials and environmental conditions on plastic shrinkage cracking were investigated. it can be concluded as following : 1 ) there was a critical w / c ratio of maximum plastic shrinkage cracking between lower and higher w / c ratio of concrete mixtures made with the same cement content per cubic meter, concretes with lower or higher w / c ratio being less prone to plastic shrinkage cracking and the w / c critical ratio critical of maximum plastic shrinkage cracking being about 0. 5

    本文研究了配製參數、主要原材料以及環境條件對新拌混凝土塑性收縮裂縫的影響，結果表明： 1 ）單方混凝土水泥用量一定時，較低水灰比和較高水灰比對應的混凝土拌合物不易開裂，而中間某一臨界水灰比對應的混凝土拌合物開裂較嚴重，這一臨界水灰比為0 . 5 ；單方混凝土水用量或水泥漿量一定時，混凝土拌合物的塑性開裂趨勢與上述情況相似，但臨界水灰比分別為0 . 45 - 0 . 4和0 . 4 。
  8. In order to study the direct relation between oil - base drilling fluid performance and cement job quality, a new developed evaluation method ( artificial core method ) was adopted ; the effects of the oil - base drilling fluid system and its main components on the shear cementing strengths of the first and second interfaces in cementing operation were investigated ; and those of the different mix slurry ratios on the gel strength, initial set time, final set time of slurry and the compressive strength of bond cement were examined too

    摘要為了研究油基鉆井液性能和固井質量之間的直接關系，採用新建立的評價方法人工巖心法，考察了油基鉆井液體系及其主要組分對固井作業中第一、第二界面剪切膠結強度的影響規律，以及不同混漿比例下對水泥漿膠凝強度、初凝時間、終凝時間和水泥石抗壓強度的影響規律。
  9. Aminobenzenesulfonic acid super - plasticizer is selected though cement paste test, which be provided with high water - reducing property, low slump loss and good compatibility with cement. according to the request of super high early strength, admixture rf is obtained though tests to compare performances of different accelerators and admixtures. experimental research and analysis are carried out on coarse aggregate ' s grain - size effect and composite aggregate ' s bulk - density to take sensitivity of coarse aggregate into account

    通過水泥凈漿試驗比較選擇了減水率高、坍落度損失小、與水泥適應性好的氨基苯磺酸鹽高效減水劑；針對超早強的性能要求，試驗比較了不同早強劑及早強性摻合料的性能表現，研製了早強性能顯著、與高效減水劑和水泥相容性較好的rf摻合料；考慮到修補混凝土對粗集料粒徑的敏感性，對粗集料粒徑效應及混合集料堆積密度進行試驗研究與分析；並對修補混凝土的抗折、抗壓、新老界面粘結強度以及抗凍性等進行了試驗研究。
  10. Workability - design of fresh concrete was studied from rheology aspect. mortar slump flow test was further developed to evaluate properties of water - reducers and compatibility between cement and water - reducer for mortar. a method for measuring water absorbed by coarse aggregate in fresh concrete was put forward

    從流變學角度對新拌混凝土工作性進行了以下研究：進一步完善了砂漿坍落擴展度試驗方法，用於測評砂漿中減水劑飽和摻量及水泥對外加劑的適應性。
  11. To significantly improve both strength and durability of repair interfacial layer between old and new concrete, two attempts were firstly put forward in this thesis : ( 1 ) a kind of new modified primer would be produced by introducing shrinkage reducing admixture into cement mortar, which may both reduce the shrinkage of the interfacial layer, and lessen the content of large crystal in the repaired interface layer, accordingly, remarkably increase the van der waals force of interfacial layer

    為大幅度提高新老混凝土修補界面層的強度和耐久性，本文首次提出並實現兩個設想： （ 1 ）以國產減縮劑為外加劑，配製新型改性水泥砂漿界面劑。該界面劑既能減少界面層宏觀干縮裂縫，又不增加大晶體，使界面層形成密實的微細觀結構，顯著提高粘結界面層內晶體間的范德華力。
  12. The flexible fiber reinforced concrete is a new kind of civil engineering material. because of its excellent performance compared with traditional concrete, it is used extensively in civil engineering

    柔性纖維混凝土是一種新型的建築材料，它以水泥砂漿或者混凝土為基體，以連續的或者非連續的纖維作增強材料。