缺口裂度 的英文怎麼說

中文拼音 [quēkǒulièdù]
缺口裂度 英文
notch acuity
  • 缺 : Ⅰ動詞1 （缺乏; 短少） be short of; lack 2 （殘缺） be missing; be incomplete 3 （該到而未到） be ...
  • 口 : Ⅰ名詞1 （人或動物進飲食的器官; 嘴） mouth 2 （容器通外面的地方） mouth; rim 3 （出入通過的地方） ...
  • 裂 : 裂動詞[方言] （東西的兩部分向兩旁分開） open
  • 度 : 度動詞[書面語] （推測; 估計） surmise; estimate
  • 缺口 : 1. （物體邊緣缺掉一塊） breach; gap; loophole 2. （不足;缺額）insufficiency3. [機械工程]notch
  1. The advantages of this modified technique can be stated as follows : ( 1 ) healing was apparently faster. ( 2 ) postoperative pain was minimal. ( 3 ) depth of vestibular fornix was increased markedly. ( 4 ) frenum and muscle attachment pull almost completely relieved. ( 5 ) there was less possibility of exposing a dehiscence or creating bone 1055 on adjacent teeth. ( 6 ) a function - ally adequate zone of attached gingiva was numerically increased

    本改良法的優點，可歸納以下幾點: （ 1 ）手術傷口愈合快（ 2 ）術后疼痛小（ 3 ）口腔前庭寬度明顯增加（ 4 ）頰系常及肌肉的拉扯，幾乎獲得完全改善（ 5 ）不易引起手術區周圍齒槽骨的裂開缺損（ 6 ）固著性齒齦寬度的增加至為明顯。
  2. Heat - sink and package datum, pad spacing, gap, length, width, spread, tweeze, missing, broken or un - plated pad

    吸熱和封裝數據，襯墊間距，裂口，長度，寬度，伸展，鑷子除去，缺少的，斷掉的，未電鍍引線
  3. Influence of loading rate on critical event of cleavage fracture in notched specimen of low alloy steel

    加載速度對低合金鋼缺口試樣解理斷裂臨界事件的影響
  4. Analysis results of histogram statistics and section electron microscopic scan technique, are that fracture feature of the cracks of the hbbb is similar and the crack is multi - source strain fatigue one. internal defects of the cast, such as impurities, gas holes, etc, are the main causes for early cracks. the contrast analysis of static strength, model and transient respond on three structures with fem proves that geometrical stress concentration in partial area has influence on early crack, also

    利用直方圖等統計方法和電鏡掃描技術對該抱軸箱體裂紋分析的結果是：抱軸箱體的裂紋斷口特徵相近，裂紋性質屬于多源性低周疲勞裂紋，鑄件中的夾雜、氣孔等內部缺陷是導致過早裂損的主要原因；利用有限元法對該抱軸箱體三種結構的靜強度、模態和動態響應對比分析，證實了局部幾何性應力集中對過早裂損也有一定影響。
  5. Nondestructive testing is a very important and difficult research lesson about the defect of concrete structures. this paper mainly measures the stress waves conveying in concrete structures and the depth of surface - opening cracks in concrete plates by using impact echo method after carefully reading a lot of articles about the state and the abroad of concrete nondestructive in the field and incorporating the special conditions on the laboratory

    混凝土結構物的缺陷的無損檢測是一個非常重要而又非常困難的研究課題，本論文在大量參閱了國內外關于混凝土結構物無損檢測的研究資料后，結合本實驗室的具體條件，應用沖擊反射法集中對應力波在混凝土板塊內傳播速度和混凝土結構物內部開口裂紋深度的測量等一系列問題展開了研究。
  6. The results showed that the notched impact strength of pvc / acr blends was improved remarkably and the tensile strength and the flexural strength of the blends have not obviously changed. the notched impact strength of pvc / acr blends was increased to about 3 times more than the pure pvc when the ratio of pvc / acr is 100 / 6 ( wt )

    結果表明，所合成的acr和pvc共混后能提高pvc的抗沖擊性能，並呈現明顯的韌性斷裂特徵，而材料的拉伸性能和彎曲性能下降不大，當pvc acr = 100 6時，共混體系的缺口沖擊強度較純pvc提高3倍多。
  7. Secondly, according to the theory of impact echo method examining flaws, the road surface and the bridge surface are aimed as study targets, four concrete plates are made with differently deep surface - opening cracks. using the experimental system of impact echo method made by sansalone etc., this paper measures the stress waves velocity conveying in concrete plates by using one transducer or two transducers, and measures the depth of surface - opening cracks in concrete plates by using two transducers, and then the important data are attained

    接著，根據沖擊反射法檢測結構物缺陷的原理，以路面和橋面的開口裂紋為研究對象，製作了帶有不同深度開口裂紋的混凝土板塊，使用sansalone等人開發的沖擊反射法實驗系統，用單傳感器和雙傳感器分別對混凝土板塊內應力波傳播的速度和不同深度的開口裂紋進行了測量，得到了重要的實驗數據。