陰極介層 的英文怎麼說
中文拼音 [yīnjíjiècéng]
陰極介層
英文
cathode interlayer-
The result shows that with the addition of rare earth elements, ultrasonic irradiation and magnetic field, the chemical component, surface configuration, microstructure and properties of electroless co - ni - b and co - fe - b alloy changes remarkably. such kind of change can be described as the followings. firstly the depositing speed of electroless alloy bath is raised while the polarizability and cathodic overpotential are reduced ; secondly the surface quality of the alloy coating and adhesion of the coating and matrix are improved ; thirdly in the coatings the content of the elements in the transient group increases, but the content of cobalt decreased ; fourthly the amorphous structure is transformed to microcrystal structure and polycrystal structure ; fifthly the microhardness and wear resistance of the coating are enhanced ; sixthly coercitive force is reduced, and magnetoconductivity of the coating is increased ; lastly the magnetic intensity of the coating increases with the addition of energy and light rare earth elements such as ce, la and decreases with the addition of heavy rare earth elements such as y. on the other side, when the alloy coatings passes through the heat treatment under the temperature of 250 or 500, their properties will change
結果顯示化學沉積co - ni - b 、 co - fe - b工藝在稀土元素( ce 、 la 、 y 、 dy ) 、能量(超聲波、磁場)介入后,沉積過程、合金成分、鍍層形貌結構和性能都有顯著變化,表現在:鍍液的陰極極化過電位和極化度降低,沉積速度提高;鍍層的結合力、表面質量改善;鍍層中過渡族元素的含量增加,輕元素硼的含量降低,同時證實了稀土元素與過渡族元素共沉積的可能性;鍍層的顯微結構由非晶態向微晶和多晶態轉變;鍍層的顯微硬度與耐磨性提高,力學性能優化;鍍層的矯頑力降低;磁導率提高;鍍層的磁化強度在能量(超聲波、磁場)和輕稀土元素ce 、 la介入后提高,重稀土元素y介入后降低。Ir - ta - ti metal oxide coated titanium anodes of variable composition were prepared by thermal decomposition. their micro morphorogies and electrochemical properties were characterized by scanning electron microscope, open circuit potential, cyclic voltammetry, consumption rate measurements and accelerated life test. the sem results indicated that all coatings were of a porous and cracked - mud microstructure influenced greatly by the composition of coatings. the electrochemical measurements showed that the ir - ta - ti ternary oxide - coated anodes exhibited excellent electrochemical activity and electrochemical stability in both acidic media and seawater which were affected by the composition and microstructure of the coatings. owing to good corrosion resistance and low consumption rate in seawater, metal oxde coated anodes belong to insoluble material, and can be potentially applid in impressed current cathodic protection systems as an anode
採用熱分解方法在鈦基體上制備銥鉭鈦金屬氧化物陽極,用掃描電鏡對陽極塗層顯微形貌進行分析,通過強化電解壽命試驗、開路電位測試、消耗率試驗及循環伏安曲線研究了金屬氧化物陽極的電化學性能. sem分析結果表明銥鉭鈦金屬氧化物陽極塗層呈現多孔多裂紋形貌結構.隨陽極塗層組成不同,塗層顯微形貌表現出很大差異,這種差異直接影響陽極電化學性能.電化學性能試驗結果表明銥鉭鈦金屬氧化物陽極在酸性介質和海水中具有良好的電化學穩定性和電化學活性.此外,銥鉭鈦金屬氧化物陽極在海水中的消耗率很低,屬于不溶性的陽極材料,作為外加電流陰極保護用輔助陽極具有廣泛的應用前景( 2 ) introduce separately the characteristic of the electric light sources, including led, gas lights and cold cathode fluorescent lamps, which are adopted in this system. study both photoelectric principle of the test and construction for the test system
( 2 )分別介紹了常用電光源發光二極體、氣體燈與本系統採用的冷陰極熒光燈的特性,探討了金免疫層析試條定量測試的光電機理以及定量測試系統的構建。With both crt ' s and lcd ' s virtue, fed has a bright future in all kinds of pdf. in this thesis, a new type of field emission cathode was described, that is using simple technique to deposit commercial nano - diamond powder on ti substrates, bonding diamond and ti, and form ohmic - contact by proper high temperature to form cathodes
本文介紹了一種器件結構和制備工藝簡單,易於實現大屏幕顯示,且適于批量生產的新型場發射陰極,即在金屬鈦襯底上均勻塗覆納米金剛石塗層,然後在高溫下退火處理實現兩者的牢固鍵合,並形成歐姆接觸。分享友人