The corrosion behavior of nanocrystalline ( nc ) copper bulks with various grain sizes prepared from igc ( inert gas condemsation ) and vacuum annealing in comparison with conventional microcrystalline ( mc ) copper ( as - rolled and electrolytic ) in acid copper sulphate solution and neutral solution containing chlorides under free corrosion conditions and anodic polarizations has been studied using potentiodynamic polarization, potentiometric analysis, cyclic voltammetry and electrochemical impedance spectroscopy. x - ray diffraction was used to estimate the grain size of the annealed nc copper. field emission gun scanning electron microscopy and x - ray energy - dispersive spectroscopy was used to characterize the surface morphology and analyze the surface composition after the polarization and potentiometric test of both nc and mc copper
本文研究了用igc （惰性氣體蒸發凝聚原位溫壓法）制備並真空退火到不同晶粒尺寸的納米晶銅和微米晶銅（冷軋紫銅、電解銅）在酸性硫酸銅溶液和中性含氯溶液中，在自腐蝕狀態和陽極極化狀態下的腐蝕性能。使用了動電勢極化、電位測定、循環伏安法（ cv ）和電化學阻抗譜（ eis ）等方法。 x -射線衍射（ xrd ）的方法用來估算納米晶銅晶粒尺寸。 -
In acid copper sulphate solution, the nc copper has a more negative corrosion potential which is decreasing with reducing the grain size and diffusion impedance was only found in the as - prepared and as - annealed at 180 ? nc copper due to the diffusion within the pores and channels on the surface. both the tafel plots and eis study demonstrated that the nc copper exhibits a higher corrosion current and lower polarization resistance than its mc couterpart
在酸性硫酸銅溶液中，納米晶銅的腐蝕電位比微米晶銅要負，並且隨著晶粒尺寸的減小而降低。 eis研究表明，未退火的和180退火的納米樣品中發現了擴散阻抗，與表面孔洞和通道中的擴散有關。極化曲線外推法和電化學阻抗研究都表明納米晶銅的腐蝕電流比微米晶銅高，而極化電阻要低。 -
The results indicated that, the fabrication process of ultra - fine grain material is mainly determined by the stress, rotate speed and the flux of cooling water. the grain refining and the hardening effect are mostly affected by the rotate speed and the flux of cooling water. compared with commercial ly12, the invalidate strength and the prolongation rate of the ultra - fine grain material are properly improved in the measurement of compression property ; and the abrupt change of the dilatability of the ultra - fine grain material at 500c is found ; also the phenomena of which the grain size of these microstructures is stable when annealed under 300c is observed
研究表明，採用本文提出的摩擦壓扭強變形區轉移法可以得到棒狀的超細晶材料，軸向壓力、扭轉速度和溫度是採用該方法制備超細晶材料的主控參數；試件的旋轉轉速和冷卻速度對變形區晶粒細化和硬化效果影響顯著；超細晶ly12的壓縮性能與淬火+自然時效狀態的ly12壓縮性能相比，斷裂強度和延伸率均有一定程度的增強；超細晶ly12的熱膨脹系數在550左右發生明顯的變化。 -
The results show the grain size becomes larger along with elevated temperature and the grain size in interconnects does not change evidently after annealed at 200 ? because of the effect of the trench structure
結果顯示熱處理后銅膜晶粒長大，但銅互連線薄膜由於溝槽結構對晶粒的長大有阻礙作用。利用xrd和ebsd測試方法對銅膜及銅互連線薄膜的織構進行評價。