球磨粉末-
Firstly, the mechanism of the preparation of superfine quartz powder with ball mill is studied in this article, based on nature of quartz material, griffith ' s strength theory and the crush theory of planetary ball mill. the problem of granulation during the process of the preparation of superfine quartz powder is studied minutely. and proposed increasing dispersant and disperser medium to restrain granulation, and dispersing use ultrasonic after milled
首先，本文結合石英材料的基本物性，以格里菲斯強度理論和行星式球磨機的粉碎原理為基礎，研究了球磨法制備超細石英粉體的機理，同時對粉石英制備過程中的團聚問題及其控製作了細致的研究，提出粉磨過程中增加分散劑和分散介質來抑制團聚，粉磨后採用超聲法進行分散，並確定了最佳分散劑、分散介質的用量和最佳超聲分散時間。 -
The cementing metal and carbon nanotubes ( cnts ) were added into the milled solid solution of w - c. by ball milling not only the additives were well dispersed in the the powder but also the size of cementing metal crystal was reduced, which was in favor of the reinforcement of alloys
在w _ （ 50 ） c _ （ 50 ）球磨製得的粉體中直接加入粘結金屬和碳納米管，利用高能球磨混合，提高它們在粉體中的分散程度的同時可以進一步減小粘結相的晶粒尺寸，有利於提高材料性能。 -
Experimental results show that the grains were gradually triturated to namometer size with milling time and the grain size might be 30nm or so, but the grain size was not decreasing after the powder has been milled for 25 hours. the nano - sized sic was synthesized by ball milling of si and c mixed powders which rare earths as a additive was added to
結果表明：隨著時間的延長，粉末逐漸細化至納米級，可以細化到30nm左右，但球磨時間超過25h后粉末顆粒繼續細化的速度明顯放慢，並且在球磨的過程因為晶粒細化和晶粒內部發生了嚴重的晶格畸變，納米粉體x射線衍射峰產生嚴重寬化。 -
Namometer silicon carbide powder was prepared from industrial silicon carbide by high energy ball milling. then the morphology and the phase structure of the milled powder were inspected by y - 4a xrd and philips xl30 peg sem., the variational rules of milled sic powder size were determined
用philipsxl30feg型掃描電鏡、 y - 4a型x射線衍射儀對球磨后的粉末進行了形貌觀察和相結構分析，統計了sic粉體尺寸隨球磨時間的變化規律。