casting strain 中文意思是什麼
casting strain
解釋
鑄造應變-
During the temperature fields, the results indicate that the processing parameters such as the extrusion velocity, casting temperature, perform preheating temperature, die preheating temperature and so on are important for the temperature fields besides the dwell time. they are must be in concordance each other to the deforming zone is in the quasi - solid state, and the stable semi - solid extrusion is implemented. during the deforming fields, the hyperbolic sine thermo - rigid - viscoplastic fem model is selected according to the forming feature of the process, and the variations of the stress - strain fields are studied
在溫度場的模擬中，模擬結果表明，保壓時間是影響製件成形質量的關鍵因素之一，擠壓速度、液態金屬澆注溫度、預制體預熱溫度和模具預熱溫度等工藝參數對溫度場的影響也很大，需進行參數之間的協調，只有當變形區內部始終維持準固態時，才能實現穩定的液-固擠壓成形過程；在變形場的模擬中，根據液態浸滲擠壓的成形特徵，選用了雙曲正弦剛-粘塑性有限元計算模型，研究了變形過程中應力應變場的變化規律，研究了模角對變形和金屬流動的影響及變形力的變化過程和其影響因素。 -
There are five parameters need to be measured. there are five channels for input : the displacement of casting - roller, the rotate speed of casting - roller, the pressure of casting and rolling, the casting temperature and the water - speed of cooling water. they are measured by raster, photoelectric coder, strain pressure sensor, thermocouple and turboflowmeter
系統需要進行監測的參數有五個，即有五路輸入信號：鑄輥位移、鑄輥轉速、鑄軋壓力、澆鑄溫度、冷卻水流速，分別採用光柵、光電編碼器、應變式壓力傳感器、熱電偶和渦輪流量計作為檢測元件。 -
In this paper, with the available computer method, theauthors have obtained the stress distribution acrosssections of reinforced concrete composite beams under two stages ofloading, and show that the stress redistribution under two stages ofloading results in a reduction of stress discrepancy in thetensile steel and of strain discrepency in the compressed concrete between thecomposite beam and the corresponding casting beam
本文運用成熟的電算模擬方法，計算得到二階段受力鋼筋砼疊合梁在不同受力階段的截面應力分佈規律及鋼筋的應力變化規律，分析得到二階段受力時鋼筋砼疊合梁1的受拉鋼筋應力超前、受壓區砼應變遲后逐漸緩解的實質為截面應力重分佈的結果 -
The segregation mechanism of tramp element sn during continuous cooling and isothermal aging and its influence on the hot ductility of low carbon steel are discussed and the brittleness during continuous casting of the sn - doped low carbon steel is forecasted. at a strain rate of 10 - 2s - 1 and a cooling rate of 10 / s, there exists a third ductility trough for both steels at 750
在應變速率和冷卻速率分別為10 ~ （ - 2 ） s和10 s的條件下進行熱模擬拉伸時，兩種試驗鋼均在750時出現由先共析鐵素體沿奧氏體晶界呈薄膜網狀析出所引起的第類脆性谷底。