摻加 的英文怎麼說

中文拼音 [chānjiā]
摻加 英文
addition
  • 摻 : 摻動詞[書面語] （持; 握） hold
  1. The result of experiment shows that und er the conditions of proper ai r - entraining, concrete with 20 % fly ash has excellent frost - resistance. the frost - resistance of concrete with 55 % fly - ash which is admixed with united expansive agent ( uea ) has been improved greatly. the frost - resistance of sulfate aluminate cement concrete with high volume of fly - ash is dramatically lower than that of silicate cement concrete with the same volume of fly - ash

    試驗結果表明：粉煤灰摻量為20的混凝土在適量引氣的條件下具有良好的抗鹽凍性能；粉煤灰摻量為55的混凝土在摻加uea膨脹劑后其抗鹽凍性能有明顯改善；大摻量粉煤灰硫鋁酸鹽水泥混凝土的抗鹽凍性大大低於同摻量的硅酸鹽水泥混凝土。
  2. Admixtures should be avoided, particularly those that are added on site.

    應當盡量避免使用摻和料，特別是避免使用須在施工現場摻加的摻合劑。
  3. Wherever possible, admixtures should be avoided, particularly those that are added on site.

    在可能的情況下，應當盡量避免使用摻加料，特別是避免使用須在施工現場摻加的摻合劑。
  4. Long term immersing marshall test and frozen - thaw cycle test were used to investigate the anti - stripping performance of andesite asphalt mixture using cement and anti - stripping agent

    摘要採取長時間浸水馬歇爾試驗和多循環凍融劈裂試驗方法，對摻加了水泥、抗剝落劑的安山巖集料瀝青混凝土水穩定性能進行研究。
  5. 7. used to add varied waste ashes and waste residue, suitable for production of high - grade encaustic tiles

    7可摻加多種廢灰廢渣，生產高質量精品彩瓦。
  6. Such methods as compounding retardants, compounding water - reducing agents ( which has various the extent of condensation ), changing the ways of addition and retardarce method, are used to impolder new water - reducing agent and construction method to salve slump loss, but it can not work drastically

    通過復合緩凝組分、不同縮合度減水劑的復合、改變摻加方式、緩釋法等技術路線開發新型減水劑和施工方法來解決坍落度損失問題，但是這一問題並沒有得到根本解決。
  7. They spiked his drink by putting a vodka in his lager

    他們在他的啤酒中摻加伏特加酒。
  8. This study is mainly to verify the strategy of restraining the neutralization by adding appropriate pozzolanic admixtures to concrete

    本研究以摻加適量卜作嵐摻料的高性能混凝土，驗證抑制中性化之策略。
  9. On the backgrounds of researches inside and outside country, and cooperating experiments with theories analyses, the influence of different processing technology parameters and different sbs modifier sorts on the sbs modified asphalts " properties has been studied. at the same time, their microstructure are observed through fluorescence optical microscopy and scanning electronic microscopy, thus to direct modified asphalt production. on the above conclusion ' s basement, analysing some disadvantages of the storage stability test of sbs modified asphalt in the current specification, a new storage stability test apparatus is developed

    本文在參考國內外研究的基礎上，採用理論、試驗相結合的方法，研究加工工藝參數以及改性劑種類等對sbs改性瀝青性能的影響，並通過熒光顯微鏡、掃描電鏡分析其微觀形態，從而指導sbs改性瀝青的生產；在此基礎上，分析我國現行規范用來評價sbs改性瀝青儲存穩定性方面的不足，開發了新的試驗儀，根據動態剪切流變試驗結果和微觀狀態分析，提出一個新的指標? ?離析率r _ s來評價sbs改性瀝青的儲存穩定性；最後，針對不穩定的改性瀝青提出改善措施，研究證明摻加增容劑和穩定劑是行之有效的方法。
  10. Here the hsc of sompa is achieved through adding super - effective water reducer, fined slag and silicon fume, and decreasing the water / cement ratio. by varying the area ( spacing ) of tension bars, compressive bars, vertical links and distribution steel and embedding steel fiber and polypropylene fiber we try to improve the behaviors of reinforced high performance concrete one - way spanning slabs in bending, so that its ductility be greater than 5. with the same arrangement of steel the width of bending member is varied to observe the effect of the width / depth ratio on the ultimate compressive strain of concrete

    通過變化受拉筋含筋率和受壓筋、箍筋（鉤筋、分佈筋）含量，或摻加纖維使之成為鋼纖維高強混凝土（ sfrhsc ）和聚丙烯纖維高強混凝土（ pfrhsc ） ，對高強混凝土雙筋截面梁、板的受彎性能進行了試驗研究，試圖改善高強混凝土受彎構件的延性，使其延性比大於5 ；並在相同配筋情況下，通過變化截面寬度，研究了高強混凝土受彎構件的寬高比對壓區混凝土極限應變的影響；並對試驗構件的裂縫發展情況進行了觀測。
  11. Paper faced gypsum board is mainly made of construction plaster ( calcined with natural gypsum of chemical by product ) and protective paper, mixing with appropriate fiber, modified starch, coagulant agent, vesicant and water

    紙面石膏板是以建築石膏（利用天然石膏或化學副產品石膏煅燒制得）和護面紙為主要原料，摻加適量纖維、改性澱粉、促凝劑、發泡劑和水，經混合、成型、凝固、切斷、烘乾、切邊等工藝製成的輕質建築板材。
  12. Incorporating with mineral admixtures could control the tendency of evening shrinkage of hpc, but the effect is not much remarkable. and the expansive agent uea could compensate shrinkage, but different curing conditions have significant effects on the volume stabilization of hpc. it is necessary to enhance the water curing at the young age and try the best to prolong the curing time

    本文對高性能混凝土體積穩定性的特點及其補償措施進行了系統的研究，主要包括：指出了水膠比對高性能混凝土體積穩定性的影響；分析了摻礦物外加劑高性能混凝土體積穩定性的特點；研究了聯合摻加礦物外加劑和膨脹劑對高性能混凝土收縮的補償效果；探索了用膨脹型中熱水泥來配製高性能混凝土對收縮的改善。
  13. Among them, working procedure optimization of construction of passing water gap in flood season in the same construction can be spread ; utilization of experience that lime dusts are mixed with macadam to satisfy winner construction, difficult problem of short construction stage in the cold area can be solved, this experience has the popular adaptability

    其中度汛期過水缺口部位施工工序的優化在同類工程中具有推廣價值；利用碎石摻加石粉料滿足冬季施工的經驗解決了寒冷地區施工期短的難題，該經驗具有普遍的適應性。
  14. This kind of adglutinate mixed with u expansion admixture can grip anchor bolts tightly even underwater, as can be seen from the pull - out type tests for anchor bolts when the mortar age is over 10 days. ( 2 ) the author lays the supporting piles as a arched shape

    將摻加了u型微膨脹劑的砂將作為錨桿水下膠結物，由錨桿齡期10天的抗拔試驗結果可以看出，這種膠結物的握裹效果很好。
  15. Abstract : the result of experiment shows that und er the conditions of proper ai r - entraining, concrete with 20 % fly ash has excellent frost - resistance. the frost - resistance of concrete with 55 % fly - ash which is admixed with united expansive agent ( uea ) has been improved greatly. the frost - resistance of sulfate aluminate cement concrete with high volume of fly - ash is dramatically lower than that of silicate cement concrete with the same volume of fly - ash

    文摘:試驗結果表明：粉煤灰摻量為20的混凝土在適量引氣的條件下具有良好的抗鹽凍性能；粉煤灰摻量為55的混凝土在摻加uea膨脹劑后其抗鹽凍性能有明顯改善；大摻量粉煤灰硫鋁酸鹽水泥混凝土的抗鹽凍性大大低於同摻量的硅酸鹽水泥混凝土。
  16. Firstly, this paper expounds the research on the physical and chemical performance of pumice and the action of those performance to pumice concrete, and the adaptability of calcium lignosulfonate to pumice concrete, and the influence of air - entrained agent to the performance of pumice concrete

    本文首先對浮石的物理、化學性能及其對混凝土的影響進行了系統試驗與研究；並進行了減水劑對浮石混凝土的適應性，以及摻加引氣劑對浮石混凝土性能的影響的分析研究。
  17. Paper faced gypsum board is mainly made of construction plaster calcined with natural gypsum or chemical by - product and protective paper, mixing with fiber, modified starch, coagulant agent, vesicant and water. which are mixed, formed, coagulated, cut, dryed and sliced into light construction material. they have advantages of light weight, fire resistance, soundproof, damp proof, heat insulation, easy to operate sawn, nailed or milled an disassemble. it s widely applied in industrial and civil constructions, especially widely used as interior wall, less loading wall, ceiling etc in high buildings

    紙面石膏是以建築石膏利用天然石膏或化學副產品石膏煅燒制得和護面紙為主要原料，摻加適量纖維改性澱粉促凝劑發泡劑和水，經混合成型凝固切斷烘乾切邊等工序製成的輕質建築板材。
  18. In this paper, the early hydration processes of cement pastes including various contents of coal stone were studied by alternating current impedance spectroscopy

    摘要採用交流阻抗譜方法對摻加不同量煤矸石的水泥漿體的早期水化過程進行了研究。
  19. Adding air - entrained agent can enhance the heat preservation performance of pumice concrete and improve its durability. using water - reducing admixture can improve the performance of pumice concrete, but the quantum is bigger than in the ordinary concrete

    為獲得良好的物理力學性能並提高混凝土的和易性，摻加減水劑對其性能改進具有明顯的技術經濟效果，其摻量要比普通混凝土稍高。
  20. The major performances of concrete and mortars, which are mixed with different quantities of expansion admixtures under the same mix proportions, are studied systematically and deeply in this work. sulphoaluminate mixed with a type of new expanding component by use of the composite methods are studied in the laboratory, and some achievements have been obtained. the service conditions, the characteristics and the shortcomings of expansion admixture in the concrete engineering are analyzed and summarized based on literatures, and the expanding mechanism of concrete is discussed

    本文試圖從膨脹劑不同摻量研究其對混凝土和砂漿主要性能的影響，進行了一系列宏觀力學性能試驗研究；利用差熱分析（ dta ） 、掃描電子顯微鏡（ sem ）等分析手段對鈣礬石等水化產物的結晶和生成量、形貌特徵進行微觀分析；並採用復合方法摻加新型膨脹組分對硫鋁酸鹽類膨脹劑（ uea ）進行了改性試驗研究，根據多因素模糊綜合評價方法就各類膨脹劑的主要性能進行綜合評價，得出摻加新型膨脹組分pt的膨脹劑性能較優，取得了明顯的效果。