無壓硫化 的英文怎麼說
中文拼音 [wúyāliúhuà]
無壓硫化
英文
non-pressure cure-
The optimum conditions for air electrode preparation were shown as follow : 20 % ptfe and 20 % mno2 in active layer, thickness of active layer 0. 15 - 0. 25mm and the ratio of active carbon to ethine black 4 : 1 ; 60 % ptfe in the gas diffusion and waterproof layer, employing na2so4 as pore - making agents, thickness 0. 35 - 0. 45mm, colding forming and layer sequence catlytic layer / gas diffusion and waterproof layer / current collector layout ; employing 40 meshed nickel screen as current collector and thermal treatment temperature over 200
確定了制備空氣電極的優化工藝條件,催化層中ptfe含量約20 , mno _ 2的最佳含量約為20 ,催化層中活性炭和乙炔黑的比例為4 : 1 (質量比) ,厚度在0 . 15 - 0 . 25mm之間。防水透氣層中ptfe的含量約為60 ,以無水硫酸鈉作為造孔劑,厚度一般為0 . 35 - 0 . 45mm 。電極各層採用催化層/防水透氣層/集流體的排布方式,冷壓成型,熱處理對空氣電極的性能影響較大,熱處理溫度不低於200 。Making sensitive material : made in non - sulfur vulcanization system with the formula : epdm 100kg, dicumylperoxide ( dcp ) 2kg as cross - linking agent, stearic acid 1kg as processing aid, oxidized zinc ( zno ) 3kg as accelerant, wax oil 10kg as lubricant ; and made in vulcanizing condition : vulcanizing temperature 170 c, vulcanizing time 15minutes, vulcanizing pressure 3 mpa, the vulcanized epdm is optimal sensitive material for petrol. the sensing head equipped with the vulcanized rubber possesses two qualities : better swelling response and better anti - interfere against temperature variation
敏感材料的制備:用無硫硫化體系;配方為:生膠100kg , dcp2kg ,硬脂酸1kg , zno3kg ,石蠟油10kg ;硫化條件:硫化溫度170 ,硫化時間15分鐘,硫化壓力3mpa ,制備的硫化橡膠對汽油的監測較理想,用其裝備的傳感頭不僅有較好的溶脹響應性能,而且有很好的抗溫變干擾能力。Servo control computer system / microcomputer universal testing machines, ozone tester, compression flexometer, computer hdt / vicat tester, digital impact tester, melt flow indexer, moving die rheometer, mooney viscometer, lamination of pvc plastic press tester
伺服控制電腦系統微電腦式拉力試驗機,耐臭氧機,橡膠壓縮生熱試驗機,塑料用維卡熱變形,數位沖擊試驗機,塑膠熔體流動速率機,無轉子密閉膜腔硫化儀,門尼黏度試驗機等等。By using the high pure alumina micro - powder ( > 99. 0 % ) and the polymorphous alumina fiber as materials, by adding alumina sulfate as the binder or polypropylene - amide as the disperser respectively, through mixing, dispersing, and compression molding, at different temperatures of 1200 c, 1350 c, 1400 c, 1500 c, and 1550 c with no pressure, the alumina fiber - alumina composites were made
本試驗採用高純氧化鋁微粉( 99 . 0 )和多晶氧化鋁纖維為原料,分別加入硫酸鋁和聚丙烯酰胺作結合劑和分散劑,經混合、分散、壓力成型及在1200 、 1350 、 1400 、 1500 、 1550下無壓燒成制得氧化鋁纖維? ?氧化鋁復合材料。Non - pressure cure