磨損阻力 的英文怎麼說

中文拼音 [mósǔnzǔlì]
磨損阻力 英文
wearing resistance
  • 磨 : 磨動詞1 （摩擦） rub; wear 2 （研磨） grind; mull; polish 3 （折磨） grind down; wear down [out]:...
  • 損 : Ⅰ動詞1 （減少） decrease; lose 2 （損害） harm; damage 3 [方言] （用尖刻的話挖苦人） speak sarcas...
  • 阻 : 動詞（阻擋; 阻礙） block; hinder; impede; obstruct
  • 力 : Ⅰ名1 （力量; 能力） power; strength; ability; capacity 2 [物理學] （改變物體運動狀態的作用） forc...
  • 磨損 : wear and tear; abrasive wear; abrase; abrade; detrition; wear; scuff; wear out; fray; battering; ...
  • 阻力 : 1 （阻礙事物發展的外力） obstruction; resistance 2 [物理學] resistance; drag; drag force; nowel; ...
  1. Gas permeability tester and mechanical folding device were developed to study the barrier property and deformation failure behaviors. the surface characterization, chemical structure, optical, mechanical properties of pet coated with dlc have been investigated by x - ray photoelectron spectroscopy ( xps ), contact angle measurement, light transmission analysis, nanoindentation and friction wear tests

    通過x射線光電子譜分析、接觸角測定、光學透過率分析、納米壓痕、摩擦磨損試驗、機械彎折試驗、氣體透過率試驗，對膜層的表面特徵，光學、力學及氣體阻隔性能進行了系統的研究。
  2. The crucial technologies of highly - displacement well mainly include torque / friction and wellbore trajectory control tool, and these technologies require rock bit have the following characteristics : having gage protection ability, long axletree lifespan, wear - resisting shirt - tail and head o. d., and high - temperature - resistant sealed system, etc

    大位移井的關鍵技術主要有扭矩摩阻和井眼軌道控制工具，這些技術要求鉆頭具有以下特點：具有良好的保徑能力，軸承壽命長，掌尖和掌背部位耐磨損，密封系統耐高溫等。
  3. Plastic deformation happened in the worn surface where fe element was found, so pam micro - fiber supported part of the load and prevented the further deformation. on the condition of high speed and high load, the worn surface of pam1 / nylon 6 composites was nearly melted and formed comparative uniform transfer on the surface of steel, which accounted for the rather low wear mass loss. the infrared analysis showed that the a small quantity of transition of crystal form from into of nylon and its composites happened during the friction because of the high temperature and strong sheering strength

    通過對復合材料耐磨性能研究表明：復合材料的摩擦系數隨載荷的增加而逐步下降，且磨損表面有明顯的塑性變形；從能譜分析結果來看，復合材料表面有fe的存在，表明pam微纖承受了部分載荷，並阻止了基體的進一步塑性變形及粘著轉移；在高速高載時， pam1 /尼龍6磨損表面處于粘流態，並在鋼環表面形成了連續的轉移膜，表現出較好的耐磨損性能，且在高溫和強剪切力的作用下，材料基體發生了少量的晶體向晶體的轉移。
  4. With the developing highway communications, the traffic is increasing and axle is becoming heavier and heavier, all of these demand the high quality of cement concrete pavement the experience of past ten years in highway construction shows that the practical life time of cement concrete pavement is far more shorter than anticipated. damages such as cracking are offen occurred in first serval years they caused direct and indirect economic losses and bad social influences. in addition to control overloaded vehicles by means of administration, the compressive strength, bending strength wear - ability should be improved to solve all these problems

    十幾年的高等級公路建設實踐表明，水泥路面的使用壽命遠遠小於其設計壽命，往往在通車幾年後就出現一些病害，如坑槽、斷板等病害，帶來的直接、間接經濟損失和不良的社會影響。解決這些問題，除了運用行政強制手段控制超載車輛外，必須提高水泥混凝土的彎拉強度、疲勞強度、耐磨強度、阻裂限縮能力，從而提高水泥混凝土路面的使用壽命。
  5. Preliminary treatment covers removal of larger suspended solids and heavier inorganic particulates through mechanical bar screening, gravitational sedimentation and flotation to keep the subsequent unit operations and processes from clogging and abrasion and to maintain the designed functions of the equipment

    前處理系指以機械攔截、重力沉澱、浮除等方式，將水中體積較大之懸浮固體、較重的無機性固體，或是過量的油脂等污染物先行移除，避免造成后續處理單元設備發生阻塞、磨損等現象，而影響到機械設備的原有功能。
分享友人
分享到 Line

分享到臉書