The influence of nano - al2o3 on the sintering and the properties of the si3n4 ceramics was researched in this paper. the samples with different amount of nano - al2o3 were obtained by using pressureless sintering at 1600, 1650, 1700 in the nitrogen atmosphere. the microstructure and the composition of the ceramics were determined by the means of x - ray, sem, micro - hardness meter etc. it is show that the sisty ceramics can be densified at 1650c to % percent of the theory density through the addition of nano - al2o3 ( the value could be 90 percent by other technique ). the crystalline growth of the cylindrical - si3n4 and the ratio of its longitude to its diameter are increased with the addition of nano - al2o3. a uniform microstructure and an fined crystal as well as more sialon phases can be obtained in the si3n4 ceramics through the addition of that
實驗結果表明：在碳管爐中、氮氣保護下進行燒結，添加劑為納米al _ 2o _ 3粉末時，由於納米粉末的高活性、高燒結驅動力，在1650就可使si _ 3n _ 4完全地燒結，並使其緻密度可達理論密度的96以上（比其它工藝高6左右） ；同時，納米al _ 2o _ 3地加入大大促進了長柱狀? si _ 3n _ 4的生長和發育及柱狀晶長徑比的提高，使微觀結構均勻、細化，形成了更多力學性能優異的固體? sialon相，減少了不利於陶瓷材料性能的晶間玻璃相，凈化了晶界。 -
X - ray diffraction analysis and density analysis and crystal structure analysis have been adopted to analyze the grid ’ s rough. through large numbers of experiments and practice, technological condition of gas discharge and depositional temperature and depositional pressure and depositional time of all kinds of the pyrolytic grid ’ s roughs has been gained. now we can deposit small and big grid ’ s roughs successfully
通過大量試驗研究和生產實踐，摸索並優化出不同品種規格的石墨柵極毛坯沉積的氣體流量、沉積溫度、沉積壓強、沉積時間等參數，能夠順利地沉積出性能優良的小型、大型的各類品種的石墨柵極毛坯，滿足了公司大功率及超大功率電子管的電參數要求，保證了新產品的成功開發。
分享友人