拉伸強力 的英文怎麼說

中文拼音 [lāshēnqiánglì]
拉伸強力 英文
tensile strength
  • 拉 : 拉構詞成分。
  • 伸 : Ⅰ動詞（展開） stretch; extend Ⅱ名詞（姓氏） a surname
  • 強 : 強形容詞（強硬不屈;固執） stubborn; unyielding
  • 力 : Ⅰ名1 （力量; 能力） power; strength; ability; capacity 2 [物理學] （改變物體運動狀態的作用） forc...
  1. With the filling of diabase, the mechanical properties of the composite increased first and then decreased with a top tensile strength of 56. 5mpa and a top impact strength of 70. 1mpa. these illuminated that the diabase fiber reinforced pvc composites could be used as structure materials

    復合材料的力學性能隨著輝綠巖的增加先升后降，復合材料拉伸強度最高可達56 . 5mpa ，復合材料沖擊強度最高可達70 . 1mpa ，說明輝綠巖纖維增強pvc復合材料作結構材料使用。
  2. The results from x - ray diffraction demonstrated that pp / mmtome was a fully intercalated nanocomposite, pp / mmtom and pp / ommt were partly intercalated nanocomposites, but the intercalation effect of pp / mmtom nanocomposite was better ; the crystallization characteristics of pure pp and pp / mmt nanocomposites were investigated by dsc, waxd and pom. the result of these testing showed that mmt nano - layers acted as nucleating agents for the crystallization of pp, the addition of mmt had effect on the crystallization process, leading the increasing of crystallization temperature crystallization rate and crystallinity, but also the dimension of spherulite reduced. but the formation of pp crystal did n ' t change, the formation of pp crystal in three pp / mmt nanocomposites and pure pp were a - form on the whole ; influences of three sorts of mmt on mechanical properties of pp / mmt nanocomposites were studied, as a result, the addition of mmt comprehensively improved mechanical properties of pp : notched impact strength, tensile strength and flexural properties were all increasing, but the extent of increasing were n ' t large

    通過xrd分析比較這三種pp mmt納米復合材料微觀結構得到， pp mmt _ （ ome ）屬于完全插層， pp mmt _ （ om ）與pp ommt的插層程度相近，但是pp mmt _ （ om ）相對較好；通過對純pp和三種pp mmt納米復合材料的結晶性能研究發現，蒙脫土納米片層對pp結晶產生明顯的異相成核作用，結晶能力增強，使pp的結晶溫度和結晶速率提高，結晶度增加，球晶晶粒細化，但是沒有改變pp的結晶形態，三種pp mmt納米復合材料的結晶形態都屬于晶；通過對pp mmt納米復合材料的力學性能測試得知，蒙脫土的加入全面提高了pp的力學性能，缺口沖擊強度、拉伸強度和彎曲性能都有一定程度的提高，浙江{ _業大學碩十學位論文摘要但是提高幅度都不是很大，不過ommt 、 mmtom和mmtc ） me三種蒙脫土對pp力學性能有著不同的改性作用，其中pp / mmtom最好， pp月邊mto崛次之， pp / ommt最低，這種情況主要是由蒙脫土對pp結晶性能的影響和蒙脫土的納米改性作用造成的。
  3. The mechanical tests result showed that when the mmt content is 2 % and the compatilizer content is 15 %, the pmc has best mechanical property. the izod impact strength is 16. 45 kj / m2 and the tensile strength is 35. 77 mpa, increasing 280 % and 4. 3 %, compared with pure pp. the pom photo indicated that the o - mmt can reduce the scale of spherical crystal of pp

    以am為插層劑得到的聚丙烯蒙脫土納米復合材料中，蒙脫土保持剝離狀態，但力學性能不理想，當土含量為0 . 5時，材料的沖擊強度為9 . 58kj m ~ 2 ，拉伸強度為25 . 5mpa 。
  4. Nonpolar polypropylene has bad compatibility with mmt even after organic modification to mmt. so polypropylene ( pp ) grafting acrylic acid was produced by the suspension grafting method as compatilizer. as pp / mmt nanocomposites prepared from htab modified mmt as concerned, the interlayer spacing of mmt is 4. 61nm, 4. 2nm and 4. 09nm respectively when the mmt content is 1 %, 2 % and 3 %. so, the abtained nanocomposites has intercalated structure

    當土含量為2 ，相容劑用量為15時力學性能最好，缺口沖擊強度和拉伸強度分別達到16 . 45kj m ~ 2和35 . 77mpa ，分別比純pp增加了280和4 . 3 ，蒙脫土的加入起到了增韌和增強的雙重作用。
  5. Tensile stress concentrations and strengths for notched unidirectional laminates

    割口單向疊層板的拉伸應力集中與強度
  6. Results of study show that inception voltage of electrical tree, breakdown voltage, environmental stress cracking, tensile strength and elongation at break of low density polyethylene are improved after grafting

    研究結果表明：接枝聚硅氧烷后，改性的低密度聚乙烯的樹枝引發示性電壓、擊穿場強、耐環境應力開裂性、拉伸強度及斷裂伸長率都得到提高。
  7. Abstract : this paper researches into the complex adhesive ， which was mainly made by the soy protein isolate ( spi ) and polyvinyl alcohol or polyvinyl acetate. different composition of protein and polymers can perform different characters, together with other ingredients. the factors, which are related to the first adhesive strength and adhesive strength, are mainly studied and discussed. the first adhesive strength of the complex adhesive is related to the content of spi, and the adhesive strength is related to the content of the complex adhesive. on the basis of the researching, we can make the plant fibre box for food in the future

    文摘:對大豆分離蛋白?聚乙烯醇、大豆分離蛋白?白乳膠復合膠粘劑進行了研究，採用不同混合比例及添加其他助劑，得到較好性能和可生物降解的復合膠粘劑，為製造一次性植物纖維快餐盒打下基礎.主要研究了影響這種復合膠粘劑粘接木塊的初粘力（剪切和拉伸強度）和粘接強度的因素，實驗表明： 9 . 2 %濃度的大豆分離蛋白的初粘力（剪切和拉伸強度）優於10 %濃度的聚乙烯醇膠和33 %濃度的白乳膠；大豆分離蛋白復合膠粘劑的初粘力主要與大豆分離蛋白含量有關，其最終粘接強度與膠液固含量正相關
  8. Textiles. woven articles. determination of the tensile strength and elongation

    紡織品.機織織物.拉伸強力和拉伸率的測定
  9. Through experiment and analyzing the changes of the thickness, rigidity, tensile strength and the opening rate of the conduits caused by the different kinds of coating material, the thickness of the coating and the different braiding structures, we investigate the physical and mechanical, properties of the braided conduits. the results show : the chitosan is easy to form the film structure on the surface of the conduits increasing the conduits ' rigidity clearly ; the rigidity and opening rate of the braided structure with inserted reinforcing yarn are better than the others, this will prevent the conduits collapsing and distorting effectively in the practical uses, so we select conduits of this structure for animal experiment

    在導管的物理機械性能研究方面，本課題通過塗層劑的種類（ pgla丙酮溶液和甲殼胺漿液） 、塗層劑的厚度、導管的編織結構三個方面分析它們對導管的厚度、硬挺度、拉伸強力和孔隙率等性能的影響。測試結果顯示：甲殼胺塗層易於在導管表面成膜，對導管的硬挺度有明顯提高，塗層效果較好；加筋結構神經導管在硬挺度和孔隙率方面優于其它導管，能有效防止導管在實際應用中的塌陷變形。
  10. Tensile strength and elongation, weight, elasticity, resistance to flammability and high heat levels, moisture - transport capabilities, durability, and weatherability are some examples of attributes that could be included in a technical textile performance specification

    拉伸強度、抗張伸展率、重量、彈性、耐燃性、耐高熱水平、水分輸送能力、耐久性和耐候性都包括在技術紡織的性能規范中。
  11. The response of mmcs has a turning point, associated with the initiation of interfacial debonding, which is decided by the interfacial strength. unlike the two predecessors, the evolving complaint interface ( eci ) model allows unloading of interfacial stresses

    在常響應界面情況下，復合材料橫向拉伸應力?應變曲線存在明顯的轉折點，對應于界面分離的始發點，轉折點的位置取決于界面粘結強度。
  12. The composites with different compatibilizers and nano - sio2 content were characterized by means of mechanical testing, differential scanning calorimetry ( dsc ), x - ray diffraction ( xrd ), fourier transformation infra - red spectroscopy ( ft - ir ), transmission electron microscope ( tem ), scanning electron microscope ( sem ), etc. the relation between the structure and property of the composites was discussed in this thesis

    研究了不同增容劑、納米sio _ 2含量對復合材料的沖擊強度、拉伸強度等力學性能；並利用差熱掃描量熱分析（ dsc ） 、 x射線衍射譜（ xrd ） 、紅外吸收光譜（ ir ） 、掃描電鏡（ sem ）等分析，討論了復合材料結構與性能的關系。
  13. Second, many mechanical properties are tested, for example, tensile strength and tensile modulus, flexural strength and flextural modulus and impact strength. by the analysis of the tensile stress - strain curves and the flexural stress - strain curves, the results are as follows : 1 ) the voluminal content of fibre of composite making by vacuum assistant resin injection is more than other composites. 2 ) the mechanical properties of the needlepunching nonwoven fabric reinforced polymer composite are superior to these of the calendering nonwoven fabric reinforced polymer composite

    首先，採用不同的增強材料（針刺非織造布和熱軋非織造布） 、不同的基體材料（ 961樹脂和306樹脂）和不同的成型工藝方法（手糊法、真空袋法和真空輔助成型法）製造出了一系列非織造布增強復合材料，然後對它們的拉伸強度、拉仲彈性模量、彎曲強度、彎曲彈性模量和沖擊強度等力學性能進行了測試，並分析了它們的拉伸載荷? ?位移曲線和彎曲載荷? ?位移曲線，結果表明真空輔助成型工藝能大大提高纖維的體積含量；針刺非織造布增強復合材料各項力學性能優于熱軋非織造布增強復合材料。
  14. On the basis of the research by former people, the work of this paper includes several aspects as follow : throughout a great deal of experiment of the mechanics performance of 2d weave c / sic composite materials laminated plate, we simulated the nonlinear relationship between a and e in the tensile course ; and we inspected the original damages and the damages evolvement ; and we made the statistic analyses of the tensile strength. some important conclusions have been given in the paper

    主要有以下幾個方面：在大量二維編織c sic復合材料力學常規性能的實驗基礎上得到了拉伸實驗中卸載點和卸載模量，卸載模量和加載斜率，加載斜率和應力等之間的關系，並在此基礎上得到了模擬同種材料拉伸曲線的非線性的應力?應變關系；配合我們的實驗過程進行初始損傷和缺陷的檢測以及實驗過程中材料損傷演化過程的動態無損檢測；對我們現有的二維編織c sic復合材料拉伸強度數據進行了分佈擬合。
  15. Tensile strength corresponds to the maximum tensile stress that may be sustained by a specimen

    抗拉強度是指樣品可能承受的最大拉伸應力。
  16. The test result of the rene95 sample showed that the maximum ultimate tensile strength can be as high as 1400mpa and has reached 97. 9 % of that of the sample fabricated by powder metallurgy ( pm ). the plastic elongation of the test sample can even exceed that of pm. the ultimate tensile strength of the test sample grown from single crystal substrate has surpassed 6 % of that of grown from the stainless steel substrate, at the same time the plastic elongation surpassed 40 %

    對成形試樣的力學性能測試結果表明，強度方面_ b最大為1400mpa ，已經達到了粉末冶金的97 . 9 ，塑性方面甚至超過了粉末冶金的水平；以單晶為基材的成形試樣其最大拉伸強度要比不銹鋼為基材的試樣高6 ，延伸率要高40 。
  17. Gloss. color. tensile strength. yield tensile strength flexural rigidity. flexural. elasticity. lmpact resistance. coating thichness. coating hardness. adhesion lmpact. abrasion. chemical resistance. cosfficicent of linear. thermal expan - sion thermal transmission properties. hdt

    光澤.顏色.拉伸強度.屈服抗拉強度.彎曲強度.彎曲模量.抗沖擊性.塗膜厚度.硬度.附著力.耐沖擊.耐磨耗性.耐化學性.熱膨脹系數.熱傳導系數.熱變形溫度
  18. Compared with those of as - sprayed ring, hardness and tension strength of area near processing face are increased by 45 % and 40 % respectively. friction mechanical performance of the ring is improved at large extent, and especially the wearing amount is merely 13 % of as - sprayed rings. after dual - direction cyclic pressing, the pore - closed state and the distributing of density and hardness are nearly identical in every part of ring. the friction mechanical property is close to that of single - direction - cyclic - press ring

    靠近壓力加工面部位，硬度較沉積坯提高了45 % ，拉伸強度較沉積坯提高了40 % 。雙向楔壓后孔洞閉合、密度硬度分佈都比較均勻。單向楔壓后，用壓力加工面作為摩擦面， al - 20 % si / sicp復合材料的摩擦磨損性能得到大幅度提高，尤其磨損量為楔壓前的13 % 。
  19. Simultaneity, various single fiber strength tests ( sft ) and the single fiber fragmentation techniques were discussed, and the influence of fiber surface treatment on the single fiber strength and the interface load - transfer were discussed in detail. the two parameters weibull statistic theory was used to evaluate the scattering of the tensile strength test results of three types of single fibers with different surface treatments. the following conclusions can be drawn based on the analysis of the results

    同時，文中詳細討論了單纖維強度測試實驗（ sft ）和單纖維復合材料斷裂實驗（ sfc ） ，重點討論了纖維表面處理對單纖維拉伸強度和界面載荷傳遞能力的影響；採用兩參數weibull統計理論對經過三種不同表面處理的單纖維拉伸強度的測試結果的分散性進行了評價，獲得了理想的實驗結果；分析實驗結果可得到如下結論， sft實驗與sfc實驗獲得的界面剪切強度吻合良好；經過表面處理的玻璃纖維的界面粘結情況較未經處理的玻璃纖維好；經過表面處理的玻璃纖維的界面粘結強度和單纖維拉伸強度均高於未經表面處理的玻璃纖維。
  20. Experiment results show that, with the increase of frequency and swing, the dispersing, physical and flame retardant performances are improved greatly, tension strength, impact strength and oxygen index have increased about 32 %, 39 % and 10 %, and finally arrive a steady value

    實驗結果表明：隨著振動頻率和振幅的增加，無機阻燃劑的分散性能、製品的力學性能和阻燃性能也會相應增加，拉伸強度、沖擊強度和氧指數可分別提高約32 % ， 39 %和10 % ，但其增加的速度是逐漸減少的，並最終達到一個穩定值。